White Fused Alumina White Aluminum Oxide Sandblasting Fused Alumina

• Customization: Available
• Natural Abrasive Type: Natural Corundum
• Artificial Abrasive Type: Corundum Abrasives
• Application: Metal Parts
• Function: Surface Finish
• Source: Artificial Abrasives
• Particle Size: Abrasive
• Hardness: Conventional Abrasive
• Crystal System: Hexzagon
• Colour: White
• Packing Density (g/cm3): 1.75-1.95
• Mohs Hardness: 9
• Size(mm): 8-5 5-3 3-1 1-0
• Fine(Mesh): -80,-120,-240,-320
• Transport Package: Ton Bag
• Specification: 8-5 5-3 3-1 1-0
• Trademark: Fuda
• Origin: China
• HS Code: 2818109000
• Production Capacity: 2000tons/Year

Product Description

 

Special White Aluminium Oxide

Stronger classification, high purity, white alumina

Consisting of sharp and fragile particles, specially treated to remove iron

High quality materials for unacceptable surface contamination

Used for cleaning and deburring applications such as printed circuit boards and medical devices

 

Typical Applications

Pure White Aluminum Oxide Medium for Investment Casting

Descaling of steam turbines

Surface treatment of thermal spray coating

Rust removal

Removal of hard oxides

Remove oxide skin

Heat treatment Descaling

Inscription on monument

Refurbishment of aircraft engines

Matte surface

Surface treatment

 

Specification

White fused alumina(WFA), a kind of high-grade refractories, is made from the imported quality alumina by melting above 2000 c in the electric arc furnace and cooling. It is white with the main crystal phase a-AL2O3. The white alumina produced in the titling electric arc furnace has the advantage of high bulk density and low porosity, thus the volume stability and thermal shock resistance can be improved..

 

For Refractory:White Fused Alumina(WFA or WA)is made from chemical by Higgns furnace or Tilting furnace at high temperature.It is very important raw material for advanced refractories and abrasives.Its properties are as folowing.

 

Type Properties		Lower sodium I				Middle sodium II
		Fraction(mesh) 0-1 1-2 3-5m/m		Fine(mesh) 0-180 0-320		Fraction(mesh) 0-1 1-2 3-5m/m		Fine(mesh) 0-180 0-320
		Guarantee Value	Typical value	Guarantee Value	Typical value	Guarantee Value	Typical value	Guarantee Value	Typical value
Chemical Composition (%)	α-Al2O3	≥99	99.3	≥98.5	99.23	≥99	99.14	≥98.5	98.75
	SiO2	≤0.2	0.15	≤0.3	0.22	≤0.4	0.12	≤0.4	0.19
	Fe2O3	≤0.2	0.04	≤0.25	0.04	≤0.2	0.01	≤0.25	0.05
	Na2O	≤0.15	0.12	≤0.25	0.18	≤0.4	0.35	≤0.5	0.23
Principal crystalline phase		α-Al2O3
Crystal system		Hexzagon
Colour		white
True density (g/cm^3)		≥3.95
Packing density (g/cm^3)		1.75-1.95
Mohs hardness		9
Linear expansion (1/^°C)		8.3×10^-4
Size(mm)		8-5 5-3 3-1 1-0
Fine(mesh)		-80,-120,-240,-320
Micropowder(um)		3-5 5-10
Test standard		GB/T3044-89
Packing		25kg/bag 1000kg/big bag
Usage		Refractories

Special particle size can be customized